Abstract: Stir-accelerated corrosion test of a high chromium cast iron was attempted in 0.1 mol dm-3 H2SO4 + 0.05 mol dm-3 HCl + 10 wt% SiC solution for 48 h at room temperature or at 45 ℃. The high chromium cast iron was composed of 2.8 wt% C and 27 wt% Cr and balanced with Fe. The high chromium cast iron was positioned into a 500 mL beaker with stirring of the solution at 1050 rpm using a magnetic hot plate. The corrosion rate was increased by agitating the solution. In addition, the corroded depth of the high chromium cast iron surface was increased by agitating the solution. The surface morphology of the high chromium cast iron after the stir-accelerated corrosion test revealed that a dendritic austenite phase partially remained in the corroded region after agitating the solution, indicating that solution movement during agitating could accelerate the corrosion rate of the high chromium cast iron.